Anisotropic creep properties of a single-crystal Ni3Al-based superalloy fabricated by liquid metal cooling process

Wednesday (28.09.2016)
17:00 - 17:15
Part of:

A single crystal Ni3Al-based superalloy was successfully fabricated by liquid metal cooling (LMC) process. The [001] and [111] oriented samples were prepared using the seeding technique. The microstructure evolution during heat treatment was investigated. The tensile and high-temperature creep rupture properties were studied both before and after the heat treatment. The microstructure evolution during creep was also studied intensively to figure out the deformation mechanism of crystals with different orientation. The results showed that the mechanical properties and deformation mechanism were strongly affected by orientation. The rupture life of samples with [111] orientation was five times longer as that of the samples with [001] orientation.

Prof. Dr. Jian Zhang
Chinese Academy of Sciences
Additional Authors:
  • Dr. jian shen
    Institute of Metal Research
  • Dr. zhengguo xu
    Institute of Metal Research